30%GF Modified PA66 Plastic Compounding Nylon66 for Auto Parts

• Min. Order: 500 kg
• Port: Nanjing, China
• Production Capacity: 10, 000tons/Year
• Payment Terms: L/C, T/T
• Material: Polyamide(Nylon 6.66)/PA
• Usage: Engineering Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• PA66+30%Gf: Injection Grade
• Model NO.: AG6BK-S01
• Trademark: Wondel
• Transport Package: 25kg/Bag
• Specification: Glass Fiber reinforced PA66
• Origin: China
• HS Code: 3908101190

Key feature:

30%GF
Thermal stability;     
Hydrolytic resistance;
Excellent combination property

Application:

Auto parts;
Radiator;
Fan;
Shield;
Mechanical parts;
Electronic parts

Data sheet is as below:
 

Property	Unit	Test standard	Test condition	GF reinforced PA66
				AG6BK-S01
Physical property
Density	g/cm^3	ISO1183		1.36
Filler content	%	ISO 1172		GF30
Mold shrinkage	%	ISO 294	Parallel	0.2
			Vertical	0.6
Mechanical property
Tensile strength	MPa	ISO 527	I type sample              50mm/min	175
Elongation at break	%	ISO 527	I type sample      50mm/min           gauge length 50mm	3
Flexural strength	MPa	ISO 178	23ºC10mm/min	245
Flexural modulus	MPa	ISO 178	23ºC10mm/min	8300
Izod impact strength (notched)	KJ/m^2	ISO 180	23ºC	9
Charpy impact strength (unnotched)	KJ/m^2	ISO 179	23ºC	65
Thermal property
Melting point	ºC	ISO11357-1		260
HDT	ºC	ISO 75	0.45Mpa	250
		ISO 75	1.8Mpa	245
Flammability
Flammability	Class	UL-94		HB
GWIT		IEC 60695-2-13		-
Electrical property
Surface resistivity	Ω	IEC60093		1.00E+14
Volume resistivity	Ω·cm	IEC60093		1.00E+15